Nama Produk: | GB13296 0Cr18Ni9 Tabung Stainless Steel Mulus untuk Boiler dan Penukar Panas | Kata kunci: | 0Cr18Ni9 Tabung Stainless Steel Seamless untuk Boiler dan Penukar Panas |
---|---|---|---|
Mengetik: | tabung stainless steel | Permukaan: | Dilapisi galvanis |
Bahan: | 0Cr18Ni9 1Cr18Ni9 1Cr19Ni9 | penggunaan: | Boiler dan Penukar Panas |
Bentuk: | Bentuk bulat | Panjang: | 4-12 m |
OD: | 6-159mm | WT: | 1-14mm |
Cahaya Tinggi: | stainless steel putaran tabung,stainless tube steel |
GB13296 0Cr18Ni9 Tabung Stainless Steel Mulus untuk Boiler dan Penukar Panas
Aplikasi : Boiler dan Penukar Panas
Ukuran : WT 1 ~ 14mm
OD 6-159mm
L 4-12m
Metode Produksi Baja : Pemurnian di luar proses peleburan kembali slag tanur listrik atau arc furnace
Metode Produksi Tabung Baja : Hot rolled (ekstrusi dan ekspansi) atau metode mulus ditarik dingin.
Penyimpangan yang diizinkan dari diameter luar dan ketebalan dinding
Klasifikasi | Ukuran nominal | Penyimpangan yang diijinkan | |
WH | OD | ≤140 | ± 1,25% D |
> 140 | ± 1% D | ||
S | ≤3 | -40% S | |
> 3 ~ 4 | -35% S | ||
> 4 ~ 5 | -33% S | ||
> 5 | -28% S | ||
toilet | OD | 6 ~ 30 | +0,15 -0,20 |
> 30 ~ 50 | ± 0,30 | ||
> 50 | ± 0,75% D | ||
S | D≤38 | + 20% S | |
D> 38 | -22% S |
Kelas baja dan komposisi kimia
Jumlah | Kualitas baja | Komposisi kimia % | ||||||||
C | Si | M N | P | S | Ni | Cr | Mo | Ti | ||
1 | 0Cr18Ni9 | ≤0,07 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 | 8.00 ~ 1,00 | 17.00 ~ 19.00 | - | - |
2 | 1Cr18Ni9 | ≤0,15 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 | 8.00 ~ 10.50 | 17.00 ~ 19.00 | - | - |
3 | 1Cr19Ni9 | 0,04 ~ 0,10 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 | 8.00 ~ 12.00 | 18.00 ~ 20.00 | - | - |
4 | 00Cr19Ni10 | ≤0.030 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 | 8.00 ~ 12.00 | 18.00 ~ 20.00 | - | - |
5 | 0Cr18Ni10Ti | ≤0,08 | ≤1.00 | ≤3.00 | ≤0.035 | ≤0.030 | 9.00 ~ 12.00 | 17.00 ~ 19.00 | - | ≥5C |
6 | 1Cr18Ni11Ti | 0,04 ~ 0,10 | ≤0,75 | ≤2.00 | ≤0.030 | ≤0.030 | 9.00 ~ 13.00 | 18.00 ~ 20.00 | - | 4Xc ~ 0,60 |
7 | 0Cr18Ni11Nb | ≤0,08 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 | 9.00 ~ 13.00 | 17.00 ~ 20.00 | - | - |
8 | 1Cr19Ni11Nb | 0,04 ~ 0,10 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 | 9.00 ~ 13.00 | 17.00 ~ 20.00 | - | - |
9 | 0Cr17Ni12Mo2 | ≤0,08 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 | 11.00 ~ 14.00 | 18.00 ~ 20.00 | 2,00 ~ 3,00 | - |
10 | 1Cr17Ni12Mo2 | 0,04 ~ 0,10 | ≤0,75 | ≤2.00 | ≤0.030 | ≤0.030 | 11.0 ~ 14.00 | 16.00 ~ 20.00 | 2,00 ~ 3,00 | - |
Kekerasan
Tipe organisasi | Kualitas baja | Kekerasan | ||
PBR | HRB | HV | ||
Austenitik | 00Cr18Ni10,0Cr19Ni9N, 00Cr17Ni13Mo2,0Cr17Ni12Mo2N | ≤217 | ≤95 | ≤220 |
0Cr18Ni13Si4 | ≤207 | ≤95 | ≤218 | |
Lainnya | ≤187 | 90 | 200 | |
Ferit | 1Cr17 | ≤183 | - | - |
00Cr27Mo | ≤219 | - | - |