Tempat asal: | Cina |
---|---|
Nama merek: | TORICH |
Sertifikasi: | iso |
Nomor model: | ASTM A485 |
Kuantitas min Order: | 1 TON |
Harga: | negotiable |
Kemasan rincian: | ASTM A866 Medium Carbon Anti-Friction Bearing Steel Tube untuk Otomotif dikemas dalam kemasan ekspor |
Waktu pengiriman: | 45 hari |
Syarat-syarat pembayaran: | L/C, D/A, D/P, T/T, Western Union, MoneyGram |
Menyediakan kemampuan: | 60000 Ton / Tahun |
Nama Produk: | ASTM A485 Anti-Kendur Tinggi Bantalan Baja 100CrMo7 | Kata kunci: | baja bantalan |
---|---|---|---|
OD: | 6-130mm | WT: | 1-25mm |
Panjang: | 3-12 m | Standar: | ASTM A485 |
Bentuk: | Bentuk bulat | penggunaan: | Untuk Bantalan Cincin |
Merek: | UNTUK KAYA | Finish permukaan: | diminyaki |
Cahaya Tinggi: | baja paduan tabung mulus,seamless alloy steel pipe |
ASTM A485 Anti-Kendur Tinggi Bantalan Baja 100CrMo7
Dimensi: diameter 10mm ~ 110mm
baja bantalan bulat
1, Kelas: ASTM A485-2 / DIN 100CrMn6 / DIN 1.3520 / GB / JB GCr15SiMn
2, komposisi kimia
C | Si | M N | S | P | Cr |
0,95 ~ 1,05 | 0,4 ~ 0,65 | 0,9 ~ 1.2 | ≤0,02 | ≤0,07 | 1.3 ~ 1.65 |
3. jangka waktu pembayaran: l / c atau tt
4. Istilah perdagangan: FOB, CIF / CFR / CNF
5, waktu pengiriman: DALAM 30 HARI SETELAH KAMI MENERIMA DEPOSIT 30%
6, Port: Dalian
7, MOQ: 1 MT
Karakter:
1, kekuatan suhu tinggi
2, tahan korosi suhu tinggi
3, kemampuan las yang baik
Aplikasi: sering digunakan dalam cincin, bola baja, rol, dan juga dibuat menjadi semua jenis mesin parrs yang membutuhkan kekuatan tinggi, ketangguhan tinggi, ketahanan abrasi yang tinggi seperti pengukur Spiral dan sebagainya dan sebagainya
Dokumen yang direferensikan
1) Standar ASTM:
A29 / A29M Spesifikasi untuk Persyaratan Umum untuk Batang Baja, Karbon dan Paduan, Tempa Panas
A751 Metode Uji, Praktik, dan Terminologi untuk Analisis Kimia Produk Baja
Metode Uji E45 untuk Menentukan Konten Inklusi Baja
E112 Metode Pengujian untuk Menentukan Ukuran Butir Rata-RataE381 Metode Pengujian Makro Batang Baja, Bilet, Mekar, dan Tempa
E1019 Metode Pengujian untuk Penentuan Karbon, Sulfur, Nitrogen, dan Oksigen pada Baja, Besi, Nikel, dan Paduan Kobal dengan Berbagai Teknik Pembakaran dan FusiE1077 Metode Uji untuk Memperkirakan Kedalaman Dekarburisasi Spesimen Baja
2) Standar ISO:
ISO 683 Bagian 17: Baja Ball and Roller Bearing
Kelas Baja dan Komposisi Kimia: | |||||||
Baja | C | M N | P | S | Si | Cr | Mo |
Kelas | maks | maks | maks | maks | min | ||
1008 | 0,10 | 0,30-0,50 | 0,040 | 0,050 | |||
1010 | 0,08-0,13 | 0,30-0,60 | 0,040 | 0,050 | |||
1018 | 0,15-0,20 | 0,60-0,90 | 0,040 | 0,050 | |||
1020 | 0,18-0,23 | 0,30-0,60 | 0,040 | 0,050 | |||
1026 | 0,22-0,28 | 0,60-0,90 | 0,040 | 0,050 | |||
1035 | 0,32-0,38 | 0,60-0,90 | 0,040 | 0,050 | |||
1045 | 0,43-0,50 | 0,60-0,90 | 0,040 | 0,050 | |||
4130 | 0,28-0,33 | 0,40-0,60 | 0,040 | 0,040 | 0,15-0,35 | 0.80-1.10 | 0,15-0,25 |
4140 | 0,38-0,43 | 0,75-1,00 | 0,040 | 0,040 | 0,15-0,35 | 0.80-1.10 | 0,15-0,25 |
Kelas | kondisi | Ultimat | Menghasilkan | Pemanjangan | Rockwell |
Kekuatan | Kekuatan | Kekerasan | |||
ksi Mpa | ksi Mpa | % | Skala B | ||
1020 | SDM | 50 345 | 32 221 | 25 | 55 |
CW | 70 483 | 60 414 | 5 | 75 | |
SR | 65 448 | 50 345 | 10 | 72 | |
SEBUAH | 48 331 | 28 193 | 30 | 50 | |
N | 55 379 | 34 234 | 22 | 60 | |
1025 | SDM | 55 379 | 35 241 | 25 | 60 |
CW | 75 517 | 65 448 | 5 | 80 | |
SR | 70 483 | 55 379 | 8 | 75 | |
SEBUAH | 53 365 | 30 207 | 25 | 57 | |
N | 55 379 | 36 248 | 22 | 60 | |
1035 | SDM | 65 448 | 40 276 | 20 | 72 |
CW | 85 586 | 75 517 | 5 | 88 | |
SR | 75 517 | 65 448 | 8 | 80 | |
SEBUAH | 60 414 | 33 228 | 25 | 67 | |
N | 65 448 | 40 276 | 20 | 72 | |
1045 | SDM | 75 517 | 45 310 | 15 | 80 |
CW | 90 621 | 80 552 | 5 | 90 | |
SR | 80 552 | 70 483 | 8 | 85 | |
SEBUAH | 65 448 | 35 241 | 20 | 72 | |
N | 75 517 | 48 331 | 15 | 80 | |
4130 | SDM | 90 621 | 70 483 | 20 | 89 |
SR | 105 724 | 85 586 | 10 | 95 | |
SEBUAH | 75 517 | 55 379 | 30 | 81 | |
N | 90 621 | 60 414 | 20 | 89 | |
4140 | SDM | 120 855 | 90 310 | 15 | 100 |
SR | 120 855 | 100 689 | 10 | 100 | |
SEBUAH | 80 552 | 60 414 | 25 | 85 | |
N | 120 855 | 90 621 | 20 | 100 |
1 ~ Pemeriksaan Bahan Baku Yang Masuk
2 ~ Segregasi Bahan Baku untuk menghindari campur aduk baja
3 ~ Pemanasan dan Ujung Palu untuk Menggambar Dingin
4 ~ Cold Drawing dan Cold Rolling, on line inspeksi
5 ~ Perlakuan Panas, + A, + SRA, + LC, + N, Q + T
6 ~ Meluruskan-Memotong untuk Inspeksi Pengukuran Panjang-selesai yang ditentukan
7 ~ Pengujian Machanical di laboratorium sendiri dengan Kekuatan Tarik, Kekuatan Hasil, Pemanjangan, Kekerasan, Dampak, Mictrostruture dll
8 ~ Pengepakan dan Stocking.
100% tabung baja kami diperiksa secara dimensi
100% tabung baja kami diperiksa secara visual untuk memastikan mereka memiliki kondisi permukaan yang sempurna dan tidak ada cacat permukaan.
100% eddy current test dan ultrosonic test untuk menghilangkan cacat longitudinal dan transversal.
Faq
T: Apakah Anda perusahaan dagang atau pabrikan?
A: Penemu bahan pipa baja profesional, produsen dan penyedia solusi
Q: Berapa lama waktu pengiriman Anda?
A: Umumnya 7-14 hari jika barang dalam persediaan. atau 30-60 hari jika barang tidak tersedia, dan itu sesuai dengan kuantitas.
Q: Apakah Anda menyediakan sampel? apakah gratis atau ekstra?
A: Ya, kami dapat menawarkan sampel untuk biaya gratis tetapi Anda perlu membayar biaya pengiriman.
T: Apa ketentuan pembayaran Anda?
A: Pembayaran <= 1000USD, 100% di muka. Pembayaran> = 1000USD, 30% T / T di muka, saldo sebelum pengiriman.
Jika Anda memiliki pertanyaan lain, silakan hubungi kami